Geogitter

ASPHALTEX BASALT

ASPHALTEX BASALT

ASPHALTEX BASALT is a warp knitted grid of basalt rovings with bitumen impregnation. The geogrid is resistant to high temperature during asphalt laying works, to chemically aggressive media and biochemical factors. The material has high tensile strength and high adhesion to asphalt concrete.

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, %

Width, m (maximum)

ASPHALTEX BASALT (50/50)

Basalt roving, bitumen impregnation 50/50 20×20 – 50×50 3 5,2
ASPHALTEX BASALT (100/100) Basalt roving, bitumen impregnation 100/100 20×20 – 50×50 3

5,2

Basalt reinforcing mesh is designed for reinforcing road and highway overlays to prolong the pavement lifespan by reducing the effects of reflective cracking caused by traffic loading, age hardening and temperature cycling. Pavement life between maintenance can be prolonged significantly. Basalt reinforcing mesh makes it possible to reduce thickness of asphalt concrete pavement up to 20%.
Incotelogy GmbH offers two different types of basalt reinforcing mesh for roads: with open and also with closed cells.

Advantages and benefits:

  • Higher mechanical strength and modulus, more resistive to chemical aggressive environment than E-glass mesh
  • The melting point of basalt fibers is over 1450°C. Typical paving temperatures will not cause any loss of strength or distortion which may occur with synthetic material
  • Lower application temperature than for synthetic material that is especially important for north regions
  • Lower elongation before brake than for synthetic material
  • Easily milled using typical milling equipment. Does not stretch and pull as polymer meshes
  • No special equipment is required to install the reinforcement
  • Basalt mesh is environment friendly and based on naturally occurring material that is found worldwide
ASPHALTEX GLASS

ASPHALTEX GLASS

ASPHALTEX GLASS is a warp knitted grid of glass rovings with bitumen impregnation. The geogrid is resistant to high temperature during asphalt laying works, to chemically aggressive media and biochemical factors. The material has high MD/CMD tensile strength and high adhesion to asphalt concrete.

Material Type

Composition MD/CMD Tensile strength, kn/m Mesh size, mm MD & CMD Elongation, %

Width, m(maximum)

ASPHALTEX GLASS (50/50)

Glass roving, bitumen impregnation 50/50 20×20 – 50×50 3 5,2
ASPHALTEX GLASS (100/100) Glass roving, bitumen impregnation 100/100 20×20 – 50×50 3

5,2

ASPHALTEX PET

ASPHALTEX PET

ASPHALTEX PET is a geotextile produced of high modulus synthetic yarns by warp knitting with further bitumen coating. The material has high tensile strength and strength of knots up to 60% of MD/CMD tensile strength.

Material Type

Composition MD/CMD Tensile strength, kn/m Mesh size, mm MD/CMD Elongation, % Width, m(maximum)
ASPHALTEX PET (20/20) Polyester yarn, bitumen impregnation 20/20 20×20 – 50×50 13

5,0

ASPHALTEX PET (30/30)

Polyester yarn, bitumen impregnation 30/30 20×20 – 50×50 13 5,0
ASPHALTEX PET (40/40) Polyester yarn, bitumen impregnation 40/40 20×20 – 50×50 13

5,0

ASPHALTEX PET (50/50)

Polyester yarn, bitumen impregnation 50/50 20×20 – 50×50 13 5,0
ASPHALTEX PET (60/60) Polyester yarn, bitumen impregnation 60/60 20×20 – 50×50 13

5,0

ASPHALTEX PET (80/80)

Polyester yarn, bitumen impregnation 80/80 20×20 – 50×50 13 5,0
ASPHALTEX PET (100/100) Polyester yarn, bitumen impregnation 100/100 20×20 – 50×50 13

5,0

ASPHALTEX PVA

ASPHALTEX PVA

ASPHALTEX PVA is a warp knitted grid of polyvinylalcohol rovings with bitumen impregnation. The geogrid is resistant to high temperature during asphalt laying works, to chemically aggressive media and biochemical factors.

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, %

Width, m (maximum)

ASPHALTEX PVA (50/50)

PVA roving, bitumen impregnation 40/40 20×20 – 50×50 6.5

5.0

GRUNTEXPET

GRUNTEXPET

GRUNTEX PET is a geotextile produced of high modulus synthetic yarns by warp knitting with further polyvinylchloride coating. The material is used as a reinforcing layer between sand bed and chip stone bed with content of fractions >5 mm higher than 60%.

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, % Width, m (maximum)

GRUNTEX PET (20/20)

Polyester yarn, PVC impregnation 20/20 20×20 – 50×50 13

5.0

GRUNTEX PET (30/30)

Polyester yarn, PVC impregnation 30/30 20×20 – 50×50 13

5.0

GRUNTEX PET (40/40) Polyester yarn, PVC impregnation 40/40 20×20 – 50×50 13

5.0

GRUNTEX PET (50/50)

Polyester yarn, PVC impregnation 50/50 20×20 – 50×50 13

5.0

GRUNTEX PET (60/60)

Polyester yarn, PVC impregnation 60/60 20×20 – 50×50 13

5.0

GRUNTEX PET (80/80)

Polyester yarn, PVC impregnation 80/80 20×20 – 50×50 13

5.0

GRUNTEX PET (100/100)

Polyester yarn, PVC impregnation 100/100 20×20 – 50×50 13

5.0

GRUNTEX PROSET

GRUNTEX PROSET

GRUNTEX PROSET is an anti-erosion geosynthetic material of polyester yarns with polyvinylchloride impregnation. The material is used for strengthening of slopes, embankments and shorelines, and as protection from water- and wind erosion.

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, %

Width, m (maximum)

GRUNTEX PROSET (20/20)

Polyester yarn, PVC impregnation 20/20 4.0×4.0 13

5,0

GRUNTEX PROSET (30/30)

Polyester yarn, PVC impregnation 30/30 2.5×2.5 13

5,0

GRUNTEX PVA

GRUNTEX PVA

GRUNTEX PVA is a geotextile produced of PVA rovings by warp knitting with further polyvinylchloride coating. The material is used as a reinforcing layer between sand bed and chip stone bed with content of fractions >5 mm higher than 60%:

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, %

Width, m (maximum)

GRUNTEX PVA (20/20)

PVA roving, PVC impregnation 20/20 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (30/30)

PVA roving, PVC impregnation 30/30 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (40/40)

PVA roving, PVC impregnation 40/40 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (50/50)

PVA roving, PVC impregnation 50/50 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (60/60)

PVA roving, PVC impregnation 60/60 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (80/80)

PVA roving, PVC impregnation 80/80 20×20 – 50×50 6,5

5,0

GRUNTEX PVA (100/100)

PVA roving, PVC impregnation 100/100 20×20 – 50×50 6,5

5,0

STRADEX PET

STRADEX PET

STRADEX PET is a geotextile produced of high modulus synthetic yarns by warp knitting with further polymer coating. The material is used as a reinforcing layer between sand bed and chip stone bed with content of fractions >5 mm higher than 60%.

Material type

Composition MD/CMD tensile strength, kN/m Mesh size, mm MD/CMD elongation, %

Width, m (maximum)

STRADEX PET (20/20)

Polyester yarn, polymer impregnation 20/20 20×20 – 50×50 13

5.0

STRADEX PET (30/30)

Polyester yarn, polymer impregnation 30/30 20×20 – 50×50 13

5.0

STRADEX PET (40/40)

Polyester yarn, polymer impregnation 40/40 20×20 – 50×50 13

5.0

STRADEX PET (50/50)

Polyester yarn, polymer impregnation 50/50 20×20 – 50×50 13

5.0

STRADEX PET (60/60)

Polyester yarn, polymer impregnation 60/60 20×20 – 50×50 13

5.0

STRADEX PET (80/80)

Polyester yarn, polymer impregnation 80/80 20×20 –  50×50 13

5.0

STRADEX PET (100/100)

Polyester yarn, polymer impregnation 100/100 20×20 – 50×50 13

5.0